For laboratories

Multilayer Zirconia Discs at Trade Pricing.

Pre-shaded HT and UT discs with natural esthetics, high strength and reliable performance.

High Strength Up to 1400 MPa
Natural Esthetics Multilayer Gradient
Consistent Quality Precision Sintering
Trade Pricing Volume Discounts
Zirconia discs product lineup

Our multilayer zirconia discs are designed for dental laboratories that demand both strength and beauty. With smooth gradients from high strength cervical areas to natural translucency at the incisal edge, they deliver lifelike restorations with excellent durability.

4Material OptionsST, ST White, SST, ML 3D
6Thicknesses10mm - 25mm
4Shade SystemsNatural & Aesthetic
98mmStandard DiameterWide Compatibility

Material Options

ST
Color
ST
White
SST
Color
ML 3D
Multilayer

Indications

  • Single Crowns
  • Bridges (≤ 3 units)
  • Veneers
  • Inlays / Onlays
  • Full Contour Restorations

Key Advantages

  • High flexural strength up to 1400 MPa
  • Natural esthetics with multilayer gradient
  • Consistent quality and precision fit
  • Excellent biocompatibility
  • Reliable for long-term performance

Ideal For

  • Crown & Bridge
  • Implant Restorations
  • Aesthetic Front Restorations
  • Full-Contour Solutions

Material & Composition

Material Type
Y-TZP Zirconia
Layers
Multilayer Gradient
Sintering Temperature
1450°C - 1530°C
Density
≥ 6.0 g/cm³
CTE (25-500°C)
10.0 ± 0.5 × 10⁻⁶ /°C
Chemical Solubility
≤ 100 μg/cm²

Physical Properties

PropertyST2 WhiteST White / ColorSST ColorML 3D
Translucency41%43%49%46-49%
Flexural Strength1400 MPa1100-1200 MPa600 MPa600-900 MPa
Fracture Toughness≥ 6.0 MPa·m¹/²≥ 5.0 MPa·m¹/²≥ 4.0 MPa·m¹/²≥ 4.0 MPa·m¹/²
IndicationCrown / BridgeCrown / BridgeVeneerFull Contour

Data based on internal testing; actual results may vary.

Indications

Single CrownsBridges
(≤ 3 Units)VeneersInlays / OnlaysFull Contour
Restorations

Size & Compatibility

Diameter
98 mm (Standard)
Thickness
10 / 12 / 14 / 16 / 20 / 22 / 25 mm
Compatible Systems
Roland, Amann Girrbach, Wieland, VHF

Sintering Parameters

Heating Rate
8-10 °C/min
Peak Temperature
1500 °C
Holding Time
2 hours
Cooling Rate
5-8 °C/min
Final Temperature
< 200 °C

Sintering Curve (Example)

1500°C · 2h Heating 8-10°C/min Cooling 5-8°C/min

Color System

  • ST (White)
  • ST-II
  • SST (A2 / A3)
  • ML 3D (Multilayer Gradient)

Certifications

CE 0197   CE Certified

Packaging

  • Individually sealed
  • Anti-moisture packaging
  • Label with lot number for traceability
  • 5 discs per box
Need more information?

Our team is here to help you choose the right solution for your lab.

Get Trade Quote Contact Us